Color of films: all kinds of colors
Gloss: Website data update...
Packing specification: 20±1kg/barrel
Mixing ratio: 10:1
Actual spreading rate: 4-6㎡/kg
Film thickness of coating: 25-35μm/track
Dry film of varnish: 15-20μm/track
Product Introduction:
This product adopts high-quality water-based fluororesin as the base material, mixed with a kind of two-component water-based fluorocarbon coating which is specially used for a kind of PVC material processed and modified out of weather-resistant, acid-base resistant and heat-resistant ceramic inorganic pigment. The excellent performance of this product’s coating system improves weather-resistance and color retention of PVC material, and lengthens its service life outdoors.
Craft product system:
|
Serial No. |
Coating process
|
Used product |
technological requirements |
details |
|
1 |
Technological Process（Polish） |
coarse sand fine sand |
Polish 2 order |
Substrate evenness≤50μm，Surface without hard fiber |
|
2 |
Technological Process（degrease） |
Special solvent |
Neat， without residu |
Clean out the surface stains, grease, and so on with a special solvent |
|
3 |
water-based epoxy enhanced primer |
ZF-WB410 |
Glossy and balanced，Smooth and dense |
spray 2 second，Dry film 15-20μm，4-6㎡/kg，mixed used out within 4h |
|
4 |
Dry in the air |
|
wet-on-wet，primer Surface dry |
Still standing for 10-20min |
|
5 |
Water-based fluorocarbon finishing coat |
ZF-WT320 |
Glossy and balanced，Smooth and dense |
spray 2-3 second，Dry film 25-35μm，4-6㎡/kg，mixed used out within 2h |
|
6 |
Dry |
|
room-temperature solidifying≥3d，bake 100±10℃，30±10min |
Film hard dry |
|
7 |
Water-based fluorocarbon coating varnish |
ZF-WT325 |
|
spray， 6-8㎡/kg，15-20μm |
|
8 |
Dry |
|
room-temperature solidifying≥3d，bake 100±10℃，30±10min |
Film hard dry |