Loading...
Loading...
Color of films: all kinds of colors
Gloss: Website data update...
Packing specification: 20±1kg/barrel
Mixing ratio: 10：1
Actual spreading rate: Metallic Paint 5-6㎡/kg
Film thickness of coating: dry film of metallic paint： 20-25μm/track
Dry film of varnish: 15-20μm/track
Product Introduction：
This product adopts high-quality water-based fluororesin as the base material, and is developed through being mixed with acid-resistant, alkali-resistant and heat-resistant inorganic ceramic pigment and high-performance auxiliaries. It is a kind of crosslinking consolidated two-component water-based fluorocarbon coating. Its fluorine content is high, and the performances of weather resistance, corrosion resistance and anti-pollution are excellent, which is appropriate for heavy duty fields such as ship, port-surrounding facilities, offshore platform, oil storage tank and so on.
Technical parameter：
|
Product name |
water-based inorganic zinc-rich primer |
micaceous iron intermediate paint |
two-component water-based fluorocarbon coating |
fluorocarbon coating varnish |
|
number |
ZF-WB210 |
ZF-WB220 |
ZF-W210 |
ZF-W215 |
|
Solid content，% |
≥70% |
≥50% |
≥50 |
≥42 |
|
Appearance |
Light-colored dispersion liquid |
Plain and matt |
Color dispersion of each color liquid |
Semitransparent dispersions liquid |
|
Proportion |
一 |
10:1 |
8:1 |
8:1 |
|
Surface treatment |
Derusting Sa2.5 grade |
一 |
一 |
一 |
|
Dry film |
80±10μm |
50±10μm |
30±10μm |
20±5μm |
|
Surface dry（humidity 50%） |
≤30min |
≤30min |
≤30min |
≤30min |
|
hard dry（25℃） |
≤4h |
≤4h |
≤3d |
≤3d |
|
Adhesive force，grade |
≤1 |
≤1 |
≤0 |
≤0 |
|
Alkali resistant |
一 |
一 |
≥168h |
≥168h |
|
Acid resistance |
一 |
一 |
≥168h |
≥168h |
|
Water tolerance |
一 |
一 |
≥168h |
≥168h |
|
Impact resistance，cm |
50 |
50 |
50 |
50 |
|
Practical Coverage |
3㎡/kg |
3-4㎡/kg |
4-6㎡/kg |
6-8㎡/kg |
Craft product system：
|
Serial No. |
Technological Process |
Product used |
process requirements |
Specific Details |
|
1 |
Preprocessing（Alkali washing） |
Alkaline treatment agent |
No grease on the surface of the base material |
Clean and dry surface, no water stains |
|
2 |
Preprocessing（Polish） |
Electric grinding machine |
Derusting Sa2.5 grade |
Sand blasting or Shot blasting |
|
3 |
inorganic zinc-rich primer |
ZF-WB210 |
Color、Glossy and balance，without holiday |
spray，dry firm 60-80μm， |
|
|
dry |
- |
zinc-rich primer dry firm |
room-temperature 24hor60±10℃，25±5min； |
|
5 |
micaceous iron intermediate paint |
ZF-WB220 |
Film Color、Glossy and balance，without holiday and so on |
spray，dry firm 50-80μm， |
|
6 |
dry |
- |
zinc-rich primer dry firm |
room-temperature 24hor60±10℃，25±5min；After dry abrasive papers Polish |
|
7 |
Water-based fluorocarbon primer |
ZF-WY210 |
Glossy and balance，no sagging and flooding |
viscosity of 50±10s(coating -4 cups),，dry film 20±5μm，4-6㎡/kg |
|
8 |
Dry in the air |
- |
primer Surface dry |
Stir in balance 10-20min |
|
9 |
Water-based fluorocarbon finishing coat |
ZF-W210 |
Film is level, color and gloss are balanced |
nozzle 2.0，viscosity of 50±10s(coating -4 cups)，dry film 25-35μm，4-6㎡/kg |
|
10 |
Dry |
- |
Film is completely dry (hard dry) |
Bake 80-100℃ 30±10min ，3d room-temperature solidifying |
|
11 |
Water-based fluorocarbon coating varnish |
ZF-W215 |
Paint film color、Glossy and balanced |
dry film 20-25μm |
|
12 |
Dry |
- |
Film is completely dry (hard dry) |
Bake 80-100℃ 30±10min ，3d room-temperature solidifying |