Hot Melt Fluorine Resin (PVDF) Coating Core functions
-
Excellent weather resistance, ultraviolet radiation properties, service life of more than 20 years
-
Excellent resistance to strong acids, alkalis and salts and salt spray, good self-cleaning properties of the paint film.

Widely used in multiple industries
Provide solutions according to needs
Manufacturing - Equipment & Transportation

Industrial - Marine&Chemical Engineering

Environment - Natural Energy

Construction - Social Infrastructure

Hot Melt Fluorine Resin (PVDF) Coating Technical Parameter
-
Product Technical Parameters
-
Matching cleaning agents and diluents
-
Surface treatment and painting
Consulting Technology


HG/T 3793-2019热熔型氟树脂(PVDF)涂料行业标准, AAMA2605-05美国建筑用铝型材对氟碳面漆的性能要求
Project | ||
Colour | Silver, various colours | |
Status in the container | No hard lumps after mixing and homogeneous | |
Constructability | Coating barrier-free | |
Film appearance | Flat paint film | |
Gloss (60°), ≥ | 70 | |
Fineness/μm, ≤ | 20 | |
Fluorine content/%, ≥ | 30 | |
Drying time/h, ≤ 220°C | Table dry | 0.5 |
Actual drying | 12 | |
Flow time (ISO No. 6 cup)/s, ≥ | 100 | |
Non-volatile fraction/%, ≥ | 55 | |
Opacity/(g/㎡), ≤ Light | 100 | |
Impact resistance/cm | 50 | |
Flexibility/mm | 1 | |
Pencil hardness (abrasion) | 2H | |
Grading test/level | 1 | |
Water resistance (1200h) | No blistering, no peeling, slight discolouration allowed | |
Heat resistance (90±2°C, 4000h) | No bulging, no wrinkling | |
Solvent wipe resistant (butanone) | 200 times without abnormality | |
Nitric acid resistance (68% HNO3 solution, 30min) | No anomalies | |
Hydrochloric acid resistance (20% HCL solution, 30min) | No anomalies | |
Salt spray resistance (4000h) | No blistering, no peeling, no rusting | |
Artificial ageing resistant (4000h) | No chalking, slight discolouration allowed |
HG/T 3793-2019热熔型氟树脂(PVDF)涂料行业标准, AAMA2605-05美国建筑用铝型材对氟碳面漆的性能要求
The single component can be used directly, add PVDF supporting diluent 10-20%.
HG/T 3793-2019热熔型氟树脂(PVDF)涂料行业标准, AAMA2605-05美国建筑用铝型材对氟碳面漆的性能要求
Steel surface treatment according to the national standard "steel surface rust grade and rust removal grade before painting" GB8923-88 implementation, sandblasting rust removal to achieve the national standard Sa2.5 grade, manual rust removal to achieve St3 grade.

Construction method
High pressure-airless spraying, brushing, rolling.